Saphir-Wafer

Anfrage Lagerbestand

Diameter (mm)
50.8
76.2
100
125
150
200
300

Orientation
C-Plane (0001)
A-Plane (11-20)
R-Plane (1-102)
M-Plane (10-10)

Thickness

min ≥
max ≤
14 Treffer 

AZ32004
50,8
0,1
/
99.998 %
A-Plane (11-20) ON ±0.2°
430
20
Polished (Ra<=0.3 nm)
As Lapped (Ra<1 µm)
/
1 Primary Flat. SEMI-Std.
/
None
10
10
65
/
AO32038
50,8
0,3
/
99.998 %
C-Plane (0001) ON ±0.05°
430
20
Epi-polished (Ra<=0.3 nm)
Epi-polished (Ra<=0.3 nm)
/
1 primary Flat. SEMI-Std.
/
/
10
10
25
/
AZ33005
76,2
0,3
/
99.998 %
C-Plane (0001) ON ±0.1°
500
20
Polished (Ra<=0.3 nm)
Polished (Ra<=0.3 nm)
/
1 Primary Flat. SEMI-Std.
/
None
10
/
50
/
AC36003
150
0,3
/
99.998 %
C-Plane (0001) ON ±0.1°
700
40
Polished Side A. S/D: 20/10
Polished Side B. S/D: 80/50
<=5 Å
1 Primary Flat. SEMI-Std.
/
Next to primary flat on B-side. S/D = 80/50
/
/
4
/
AZ32001
50,8
0,1
/
99.998 %
C-Plane (0001) ON ±0.2°
430
20
Polished (Ra<=0.3 nm)
As Lapped (Ra<1 µm)
/
1 Primary Flat. SEMI-Std.
/
/
10
15
221
/
AZ32033
50,8
0,1
/
99.998 %
C-Plane (0001) ON ±0.2°
430
25
Polished (Ra<=0.3 nm)
Polished (Ra<=0.3 nm)
/
1 Primary Flat. SEMI-Std.
/
/
10
10
130
/
AZ32048
50,8
0,1
/
/
C-Plane (0001) ON ±0.2°
250
25
Polished (Ra<=0.3 nm)
Polished (Ra<=0.3 nm)
/
1 Primary Flat. SEMI-Std.
/
/
10
15
24
/
AZ34041
100
0,1
/
99.998 %
C-Plane (0001) ON ±0.2°
650
25
Polished (Ra<=0.3 nm)
Polished (Ra<=0.3 nm)
/
1 Primary Flat
/
None
10
15
93
/
AZ34001
100
0,1
/
99.998 %
C-Plane (0001) ON ±0.3°
650
25
Polished (Ra<=0.3 nm)
As Lapped (Ra<1.2 µm)
/
1 Primary Flat
/
None
10
15
15
/
AZ34038
100
0,1
/
99.998 %
C-Plane (0001) ON ±0.3°
650
25
Polished (Ra<=0.3 nm)
As Lapped (Ra<1.2 µm)
/
1 Primary Flat
/
None
10
15
120
/
AO34029
100
0,3
/
/
C-Plane (0001) ±0.3°
1000
20
Polished (Ra<=0.3 nm)
Polished (Ra<=0.3 nm)
/
None
None
None
10
15
5
/
AO34030
100
0,3
/
/
C-Plane (0001) ±0.3°
1000
20
Polished (Ra<=0.3 nm)
Polished (Ra<=0.3 nm)
/
1 primary Flat. SEMI-Std.
/
None
10
15
23
/
AO34021
100
0,3
/
>99.998 %
R-Plane (1-102) ON ±0.2°
500
20
Polished (Ra<=0.3 nm)
As Lapped (Ra<1 µm)
/
1 primary Flat. SEMI Std.
/
None
10
15
12
/
AO32017
50,8
0,2
/
99.998 %
R-Plane (1-102) ±0.2°
430
20
Epi-polished (Ra<=0.3 nm)
As Lapped (Ra<1 µm)
/
1 Primary Flat. SEMI-Std.
/
None
10
15
20
/
Anfrage Lagerbestand